Heat of hydration of Bogue compounds – Maximum heat of hydration

Saad Iqbal | 🗓️Modified: December 19, 2022 | ⏳Read Time: 4 min | 👁Post Views: 110

Cement is a vital building material used in the construction of roads, bridges, and buildings around the world. While most people are familiar with cement and its uses, few are aware of the secret ingredient that gives it its unique properties: Bogues compound.

In this blog post, we’ll explore what Bogues compound is, why it’s added to cement, the heat of hydration for both cement and Bogues compound, and the four compounds found in cement.

So, read on to discover the complete story of Bogues compound in cement!

The heat of hydration for various bogues compound is:

Tricalcium Silicate C3S – Heat of hydration – 500 J/g.

Dicalcium Silicate C2S – Heat of hydration – 260 J/g.

Tricalcium Aluminate C3A – Heat of hydration – 865 J/g.

Tetracalcium Alumino Ferrite C4AF– Heat of hydration – 420 J/g.

The lowest heat of hydration is of C2S and therefore if you increase the content of C2S, the heat of hydration will be reduced.

Tricalcium Aluminate > Tricalcium Silicate > Tetracalcium Alumino Ferrite > Dicalcium Silicate

Or we can write as:

C3A > C3S > C4AF > C2S

Cement is an essential material in the construction industry, and it is important to understand how heat of hydration affects its properties. Heat of hydration is the energy released when cement combines with water during the curing process. The heat generated during hydration is a result of the chemical reaction between calcium silicate hydrates, or C-S-H, and the unhydrated components of cement (alumina, iron oxide, and gypsum).

When cement is mixed with water, it forms a paste that begins to harden as the C-S-H crystallizes, which releases heat. The amount of heat released depends on the type and quantity of cement used, as well as the amount of water present. Typically, higher concentrations of cement release more heat, while lower concentrations generate less heat.

The heat of hydration affects several important properties of the cement, such as strength, durability, porosity, and permeability. In addition, higher temperatures can cause certain additives to chemically react with the cement, potentially leading to decreased performance and strength.

As such, controlling the rate of hydration and thus the heat generated during the process is essential in order to ensure proper curing and performance of the cement. Methods such as adding water or adjusting the mix design can be used to reduce the rate of hydration and therefore control the temperature.

Maximum heat of hydration in bogue’s compounds

Cement is a fundamental building material that has been used in construction for centuries. But what is lesser known is that cement contains four compounds, one of which is called Bogues compound.

In this blog post, we’ll explore what Bogues compound is, what its role is in cement, and how it affects the heat of hydration.

We’ll also explore the other three compounds that make up cement, and what they all mean to the construction industry.

So if you’re interested in learning more about cement, or just curious about what makes it work, this is the perfect place to start.

The maximum heat of hydration in bogue’s compound is that of C3A – Tricalcium Aluminate C3A which is 865 J/g.  

Which of the following Bogue’s compounds produce maximum heat of hydration?

The bogues compound that produces the maximum heat of hydration is Tricalcium Aluminate or C3A that produces around 865 J/g of heat.

Similar Questions: The rate of heat of hydration of the bogue’s compounds in descending order is